Tungsten Carbide Ropes for max. abrasion resistance
- For overlay of drill bits& cones, stabilizers, screws, augers, bucket teeth, brick and clay dies requiring high hardness. For building up wear plates, guides, furnace pars, heat treating baskets, cams and bolt Ideal edge for industrial knives and tools such as sugar cane blades, debarker tools, paper and textile cutters, lower radial bearings, mixer blades, and other parts requiring good edge retention characteristics.
- Deposits are hard and non-machinable extremely high resistance to any combination of friction, abrasion, compressive loading, heat and corrosion,
- Made for application with oxy-acetylene flame.
- Application temperature: 1100 C
- RECOMMENDED FOR GEO THERMAL APPLICATIONS
- HARDFACING WITH 788 –G can increase the lifetime on vital parts many times, increasing production and reducing downtime
Tungsten Carbide Ropes and Rods for hardfacing against extreme Abrasion
| PRODUCT GOLD | DESCRIPTIONS/APPLICATIONS | TECHNICAL
DETAILS |
Ø
mm |
| 780 G | Tubular ROD filled with tungsten carbides, for application subject to extreme scraping abrasion.
Fan and mixer blades, screw conveyors for ash ce ment ,sand and pulp, dry cement pumps, rotary drills, drill bits ,brick dies and presses, shredder knives, ripper teeth, debarker tools (wood), stabilizers, elbows of concrete pumps. |
Hardness: HRC 60
(matrix) Carbide Hardness 2500 HV Alloy: WC/FE DIN855: G 21-Gr-60G |
3.5
5.0 |
| 788 G | Self fluxing flexible type low temperature brazing rod for anti wear coatings against abrasion, corrosion and friction. Use for maximum protection on conveyor screws, drill bits, stabi lizers, mixer blades, extrusion dies and presses………….. | Hardness:
2500-3000 HV CARBIDES ALLOY:WC/NI/Cr.Fe,B |
4.0
5.0 6.0 |
| 790 G | A torch rod containing copper, nickel and tungsten. Massive amounts of “tungsten chips” having each sharp cutting edg es. Use on oil and rock drills, rotary cutting bits, augers, drill pipes and stabilizers. Also for tools to remove drill rods in well-drilling. The following tungsten carbide chip sizes are available:
1,6 – 3,2; 3,2 – 4,8; 6,0 – 9,0 mm. |
Hardness:
2500-3000 HV CARBIDES GOOD CUTTING ACTION |
|
| 865 BB
865 FB |
Special nickel bronze alloy for high strength joining and build -ups. Use for overlay-ing and build-up of gear teeth, bear ings, shafts, valve seats, wedge bars and steering knuckles, stabilizers (with 790),rotors, pump impellor
Available as flux coated (865 FB) or bare rods.(865 BB) |
Hardness: ~200 HB
Melting range:845-865ºC |
3.0
4.0 |